Pro-Bolt DualDrive Designed for Race Teams –
The Ultimate Bolt combining form and function. Benefit from superb functionality, strength and durability! You can select the appropriate tool, depending on accessibility & torque required.
DualDrive features: Head design that is compatible with both Socket and Allen Keys. Forged Bolts with rolled threads for superior strength. Grade 5 Titanium to maximise strength and durability with fantastic weight saving properties. Pre-drilled for lock-wiring. The choice of tool and resilience of the design makes this bolt the choice of GP, WSBK & BSB race teams worldwide.
Now available in Black!!! Supreme hardness and corrosion resistance provided by nanocomposite coating. Beautiful, long lasting black finish resulting from application of Diamond Like Coating (DLC).
This workshop box contains 100 of the most popular DualDrive bolts, with prior consent from Pro-Bolt is may be possible to amend the contents slightly.
Gift Message is available on this product - enter your message at checkout and it will be etched on a plate on the front of the presentation case.
|Material||Titanium Grade 5|
|Product Type||Workshop Assortments|
|Weight in Gms||1013.9300|
|Country of Manufacture||United Kingdom|
Made from aircraft grade titanium 6AL-4V (grade 5), the outstanding benefits are that we roll the threads to produce greater fatigue strength and reduce galling. These bolts are in excess of 120,000psi ultimate tensile strength, suitable to replace both Grade 5 and Grade 8 steel bolts. We offer Race Spec drilled Flanged Hex Head Bolts, Flanged Hex Head, Tapered Socket Cap, Countersunk Bolts, Dome Head Bolts, Nuts and Washers – from 3mm to 12mm.
- Density4420kg/m3 (276lb/ft3)
- Young's Modulus 110GPa (16 x 106 psi)
- Yield Strength 828MPa (120 x 103 psi)
- Ultimate Tensile Strength 1030MPa (149 x 103 psi)
- Compressive Strength 960MPa (139 x 103 psi)
- Shear Modulus43GPa (6.24 x 106 psi)
- Ductility 10% elongation at break
- Poisson's Ratio0.34
- Hardness 36 Rockwell C
- Strength-to-Weight Ratio 187 kNm/kg
- Stiffness-to-Weight Ratio 24.9 Mnm/kg
Black Titanium: Long lasting finish resulting from an application of Diamond Like Coating (DLC). This unique finish increases the fastener lifetime and helps to prevent galling whilst providing a supreme hardness and offering the optimum in corrosion resistance thanks to a nanocomposite coating.